Polypropylene Short-Cut Fiber for Dry-Mixed Mortar and Grc Premixing

• Customization: Available
• Application: Concrete Reinforcement
• Color: White
• Model NO.: Micro Fiber
• Length: 6-18mm,Custom Length
• Material: High-strength Polypropylene Fiber
• Tenacity: High Tenacity
• Type: Microfiber
• Melting Point: 160-170
• Elastic Modulus: >5.0gpa/3.0gpa
• Tensile Strength: >500MPa/350MPa
• Elongation at Break: 15-30%/50%
• Transport Package: Carton Packing
• Specification: 3/4/6/8/12/16/18/Custom Length
• Trademark: HongLi
• Origin: Shandong, China
• HS Code: 7217301000
• Production Capacity: 30000t/Year
• Package Size: 605.80cm * 243.80cm * 259.10cm
• Package Gross Weight: 30000.000kg

Product Description

Product description
  The polypropylene fiber produced by our company is a synthetic fiber made by adding 100% modified polypropylene into the masterbatch, blending, spinning, stretching, antistatic and ultraviolet resistance. It is a special fiber of concrete and mortar, which can effectively control the cracks of concrete and mortar caused by shrinkage, shrinkage and temperature change. Amine is non-toxic, acid and alkali resistant, antimagnetic and antirust, and has strong binding force with cement. It greatly improves the crack resistance, impermeability and erosion resistance, and increases the toughness of the concrete, thus prolonging the service life.

Application area
1. Anti-crack, anti-seepage and thermal insulation mortar for industrial and civil buildings.
2. Concrete pouring projects with high impermeability and impact resistance such as working face dam, spillway and diversion hole in water conservancy and hydropower projects.
3. Various precast concrete products.
4. Concrete for roads, bridges, tunnels and airport runways.
5. Chemical plants with high requirements for alkali resistance and chemical corrosion.
 

Product Name	Model	Materials	Shape	Density	Melting Point	Equivalent Diameter	Tensile Strength	Elastic Modulus	Elongation at Break	Length(mm)
High Strength	HLBG	Modified polypropylene	Monofilament Bundle	0.91g/cm3	160-170	20-50um	>500Mpa	>5.0Gpa	15-30%	3/4/6/8/12/16/18 custom length
Hollow type	HLBK	Modified polypropylene	Monofilament Bundle	0.91g/cm3	160-170	70-100um	350Mpa	3.0Gpa	50%	3/4/6/8/12/16/18 custom length